ASTM A1092-15(R2020) pdf free download,Standard Specification for Steel Sheet, as Cold-Reduced, for Conversion to Annealed Cold-Rolled Steel Sheet, and Hot Dip Metallic-Coated Steel Sheet
1. Scope
1.1 This specification covers the requirements for as cold- reduced steel sheet in coils intended for conversion into cold-rolled steel sheet on continuous annealing lines, and metallic-coated steel sheet on continuous hot-dip coating lines. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This international standard was developed in accor- dance with internationally recognized principles on standard- ization established in the Decision on Principles for the Development of International Standards, Guides and Recom- mendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
3. Terminology
3.1 Definitions: 3.1.1 as cold-reduced steel sheet, n—an as-rolled product intended for conversion to annealed cold-rolled steel sheet product or hot-dip metallic-coated steel sheet product. Discussion—As a result of the high degree of cold reduction as cold-reduced steel sheet exhibits high tensile strength with very minimal ductility.
4. Classification
4.1 The material is in a semi-finished form intended for conversion to cold-rolled steel sheet, or hot-dip metallic-coated sheet steel whose designations are described in the following specifications: 4.1.1 A308/A308M Specification for Steel Sheet, Terne (Lead-Tin Alloy) Coated by the Hot-Dip Process,4.1.2 A463/A463M Specification for Steel Sheet, Aluminum-Coated, by the Hot-Dip Process, 4.1.3 A653/A653M Specification for Steel Sheet, Zinc- Coated (Galvanized) or Zinc-Iron Alloy-Coated (Gal- vannealed) by the Hot-Dip Process, 4.1.4 A792/A792M Specification for Steel Sheet, 55% Aluminum-Zinc Alloy-Coated by the Hot-Dip Process, 4.1.5 A875/A875M Specification for Steel Sheet, Zinc-5 % Aluminum Alloy-Coated by the Hot-Dip Process, 4.1.6 A929/A929M Specification for Steel Sheet, Metallic- Coated by the Hot-Dip Process for Corrugated Steel Pipe, 4.1.7 A1008/A1008M Specification for Steel, Sheet, Cold- Rolled, Carbon, Structural, High-Strength Low-Alloy, High- Strength Low-Alloy with Improved Formability, Solution Hardened, and Bake Hardenable, 4.1.8 A1046/A1046M Specification for Steel Sheet, Zinc- Aluminum-Magnesium Alloy-Coated by the Hot-Dip Process, 4.1.9 A1063/A1063M Specification for Steel Sheet, Twin- Roll Cast, Zinc-Coated (Galvanized) by the Hot-Dip Process, 4.1.10 A1079 Specification for Steel Sheet, Complex Phase (CP), Dual Phase (DP) and Transformation Induced Plasticity (TRIP), Zinc-Coated (Galvanized) or Zinc-Iron Alloy-Coated (Galvannealed) by the Hot-Dip Process, and 4.1.11 A1088 Specification for Steel, Sheet, Cold-Rolled, Complex Phase (CP), Dual Phase (DP) and Transformation Induced Plasticity (TRIP).
5. Ordering Information
5.1 As cold-reduced steel sheet in coils is produced to thickness requirements expressed to 0.001 in. (0.01 mm). Con- sult the producer for the option of ordering thickness to 0.0001 in. (0.001 mm). N OTE 1—When ordered to thicknesses of 0.0001 in. (0.001 mm) the Specification A568/A568M thickness tolerances expressed to 0.001 in. (0.01 mm) remain in effect. 5.2 Orders to this specification shall include the following information, as necesssary, to adequately describe the desired product: 5.2.1 Name of product (steel sheet, as cold-reduced), 5.2.2 Dimensions (show thickness, minimum or nominal, width),5.2.3 Surface finish (if required), 5.2.4 ASTM designation number and year of issue, as A1092-XX for inch-pound units or A1092M-XX for SI units, 5.2.5 Coil size requirements (specify the minimum and maximum outside diameter (OD), the acceptable inside diam- eter (ID), and maximum coil weight [mass]), 5.2.6 As cold-reduced mill edge or slit edge. If edge is not specified, the as cold-reduced edge will be furnished, 5.2.7 Packaging, and 5.2.8 Certification, if required, for heat analysis. 5.3 Identify the applicable cold-reduced steel sheet, or hot-dip metallic-coated steel sheet product specification (see 4.1), and the intended product steel sheet designation [CS (Types A, B, and C), (DS Type A and B), DS, FS (Types A and B), DDS (Types A and C), EDDS, SS, HSLAS, HSLAS-F, SHS, BHS, CP, DP or TRIP] and coating weight designation to describe the required chemical requirements. 5.4 Special requirements (if any). 5.4.1 When the purchaser requires the thickness tolerances for 3 ⁄ 8 in. minimum edge distance this requirement shall be specified on the purchase order or contract (see Specifications A568/A568M or A924/A924M, as applicable).
6. Chemical Composition
6.1 The chemical composition shall conform to the require- ments of the intended designation in the individual metallic- coated sheet and cold-rolled specification to which the product will be converted, namely Specifications A308/A308M, A463/ A463M, A653/A653M, A792/A792M, A875/A875M, A929/ A929M, A1008/A1008M, A1046/A1046M, A1063/A1063M, A1079, or A1088. 6.2 See Specification A568/A568M for chemical analysis procedures for cold-rolled product, and Specification A924/ A924M for chemical analysis procedures of metallic-coated product. 6.3 Nonstandard chemical compositions shall be as agreed between producer and purchaser. 6.4 The producer of the as cold-reduced product is respon- sible to meet all chemical requirements as agreed to and specified on the purchase order.